Um material de implante
consagrado pelo tempo

 
316LVM

This stainless steel alloy is a unique nomenclature for Fort Wayne Metals and meets all the requirements of 316LS. Mainly used for permanent implants, 316 LVM’s corrosion resistance is controlled by a reduced carbon content compared to the other 300 series alloys. The material is vacuum re-melted, giving it a more uniform chemistry with minimal voids and contaminants.

Composição química
ASTM F138
Composição %
(massa/massa)
Carbono 0.030 max
Manganês 2.00 max
Phosphorous 0,025 máx.
Enxofre 0,010 máx.
Silício 0,75 máx.
Cromo 17.00 to 19.00
Níquel 13.00 to 15.00
Molibdênio 2.25 to 3.00
Nitrogênio 0.10 max
Cobre 0.50 max
Cobalto <0,10
Ferro Equilíbrio
Composition Index = % Cr + 3.3 x % Mo 26.0 min

 

Propriedades físicas
  Métrico Inglês
Densidade 7.35 g/cm³ 0.286 lbs/in³
Modulus of Elasticity 195 GPa 28.0 Mpsi
Electrical Resistivity 720 µohms/mm 29.2 µohm/in
Thermal Conductivity 16.3 W/m-K (100°C) 9.08 BTU-in/hr-ft²-°F

*At 100 °C [212 °F].

Propriedades mecânicas
Cold worked
%
Yield strength
MPa [ksi]
Ultimate tensile strength
MPa [ksi]
Elongation
%
0 310 [45] 627 [91] 42
20 758 [110] 848 [123] 8
37 1000 [145] 1103 [160] 2.5
50 1110 [161] 1213 [176] 2.2
60 1172 [170] 1317 [191] 2.1
68 1213 [176] 1400 [203] 2.5
75 1317 [191] 1503 [218] 2.6
80 1282 [186] 1496 [217] 2.6
84 1393 [202] 1565 [227] 2.6
90 1413 [205] 1641 [238] 2.6
93 1462 [212] 1648 [239] 2.6
95 1469 [213] 1696 [246] 2.8

*All data represent results from a 25.4 cm [10 in] test gauge length. Values are typical and may not represent all diameters. Test method will affect results.

Para obter especificações detalhadas sobre 316LVM, clique aqui.

Produtos finais
  • Fio de sutura
  • Cabos ortopédicos
  • Grampos de fechamento para pele
  • Cateteres
  • Estiletes
  • Pinos para ossos
  • Peças pequenas usinadas